{"id":301,"date":"2020-08-03T13:04:51","date_gmt":"2020-08-03T13:04:51","guid":{"rendered":"http:\/\/brightalloys.com\/index.php\/products\/sibriquette-2-2-2\/"},"modified":"2025-06-16T19:09:24","modified_gmt":"2025-06-16T11:09:24","slug":"carbon-riser","status":"publish","type":"al_product","link":"https:\/\/brightalloys.com\/index.php\/products\/carbon-riser\/","title":{"rendered":"Carbon riser"},"content":{"rendered":"

For Cast Iron 1-5mm Graphite Petroleum Coke\/Carburant\/Carbon riser<\/h2>\n

For casting, cast iron, cast steel and castings will have a requirement for carbon. As the name suggests, carburizing agent is to increase the carbon content in molten iron.Using pig iron, scrap and return charge are commonly smelting,however the carbon content of pig iron is high, but the purchase price is one section higher than that of scrap.Therefore, increase the amount of scrap and reduce the amount of pig iron, adding carburizing agent can reduce the casting cost to a certain extent.<\/p>\n

Bright Alloy devote to provide iron casting,steel making industry most competitive service and reliable quality in carbon material. Our capacity of various carbon material over 2000 tons monthly,we had long steady cooperation with major steel iron program and foreign iron industry partners with full experiences.<\/p>\n

Type of Carburant:<\/h2>\n

According to the casting application,there are few types:nodular Iron carburizer, gray iron carburizer,cast steel carburizer and special steel carburizer.<\/p>\n

    \n
  1. Ductile iron suitable for the high carbon and low sulfur products with graphitized carburizing agent as carburizing agent, and the sulfur content is strictly low, which is generally as follows: s: \u2264 0.1%, s: \u2264 0.05%;<\/li>\n
  2. \u00a0The main technical index difference between gray iron carburizing agent and nodular iron carburizing agent lies in the control of sulfur. The general index requirement is s: \u2264 0.5%;<\/li>\n
  3. \u00a0The types of carburizing agents for steel casting (steelmaking) are complex. Generally, large steel plants will choose a variety of carburizing agents according to different steel grades, but the general materials are calcined coal and graphite particles or graphite balls, and natural graphite fragments,with the content ranging from 75% to 99%.<\/li>\n<\/ol>\n

    Fixed carbon and ash content are two opposite parameters in the carburizer,and they are also two important parameters affecting the carburizing efficiency.So when the fixed carbon content is high and ash content is low,the carburizing efficiency is high, otherwise, the carburizing efficiency is low.<\/p>\n

    \"graphite<\/h3>\n

    HOW TO USE of carburizers:<\/h2>\n

    1. Adding in furnace<\/p>\n

    We can adjust the amount of carburizing agent according to the carbon content of molten steel (iron) during proportioning,and the carbon absorption rate can reach 90-99% when you add the metal charge to the the electric furnace.<\/p>\n

    2. Carbon increase in later stage<\/p>\n

    After smelt molten steel (iron), you can add a small amount of carbon to the surface of the molten steel (iron). The carburizer can be dissolved and absorbed by the eddy current stirring of the molten steel (iron) during electric furnace melting and the carbon absorption rate is 80-95%.<\/p>\n

    Product advantages:<\/h3>\n

    1. The absorption rate is over 90% and the absorption rate is fast;<\/p>\n

    2. It can promote the inoculation and nucleation of cast iron;<\/p>\n

    3. Improve the graphite morphology, increase the amount of graphite, refine graphite, improve the mechanical properties of products, improve processing performance.<\/p>\n

    \"carbon<\/h3>\n

    Grades<\/h3>\n\n\n\n\n\n\n\n\n
    \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0\u00a0\u00a0 Carburant\/Carbon Additive<\/td>\n<\/td>\n<\/tr>\n
    Graphilized Petroleum Coke<\/td>\nF.C 99 min%<\/td>\nAsh 0.5%<\/td>\nV.M 0.5%<\/td>\nS 0.05%<\/td>\n1-5mm<\/td>\n<\/tr>\n
    Graphilized Petroleum Coke<\/td>\nF.C 98.5 min%<\/td>\nAsh 0.5%<\/td>\nV.M 0.5%<\/td>\nS 0.05%<\/td>\n1-5mm<\/td>\n<\/tr>\n
    Calcined Petroleum Coke<\/td>\nF.C 98 min%<\/td>\nAsh 0.5%<\/td>\nV.M 0.5%<\/td>\nS 0.3%<\/td>\n1-5mm<\/td>\n<\/tr>\n
    Cylindrical carburizing agent<\/td>\nF.C 92-95% min<\/td>\nAsh 2.5%<\/td>\nV.M 2%<\/td>\nS 0.05%<\/td>\n1-5mm<\/td>\n<\/tr>\n
    Calcined Coal carburizing agent<\/td>\nF.C 90-95%<\/td>\nAsh 3-7%<\/td>\nV.M 0.5-1.5%<\/td>\nS 0.3-0.5%<\/td>\n1-3,1-5,1-8mm<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

    \"\"<\/h3>\n
    \n

    Cylindrical carburizing agent<\/h2>\n

    Cylindrical carburizing agent, mainly used in casting, production of ordinary cast iron, gray cast iron.<\/p>\n

    According to the market feedback in the past two years, from the beginning of the manufacturers trying to use cylindrical carburizer to the past two years, the amount of use has been rising. Many manufacturers respond that under the premise of good use effect, the production cost can be effectively reduced, It is favored by many foundries.<\/p>\n

    Suitable for large furnace,the bigger the furnace, the better the melting effect and the higher the absorption rate,according to customer feedback, the absorption rate can reach 90%.<\/p>\n

    Chemical specification: fixed carbon: 92-95%, sulfur content: 0.05-0.1%;<\/p>\n

    Particle size : 1-5mm.<\/p>\n

    HOW TO USE of Cylindrical carburizing agent:<\/h3>\n

    1. Adding in furnace<\/p>\n

    The amount of carburizing agent is adjusted according to the carbon content of molten steel (iron) during proportioning. The carbon absorption rate can reach 90-99% when the metal charge is added to the lower part of the middle part of the electric furnace.<\/p>\n

    2. Carbon increase in later stage<\/p>\n

    After the molten steel (iron) is melted, a small amount of carbon can be added to the surface of the molten steel (iron). The carburizer can be dissolved and absorbed by the eddy current stirring of the molten steel (iron) during electric furnace melting. The carbon absorption rate is 80-95%.<\/p>\n

    \"carbon
    Cylindrical carburizing agent\u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0 \u00a0C 95%min,S 0.05%max,ASH 4%max,V.M 1.5%max<\/figcaption><\/figure>\n
    \n

    Graphite Petroleum Coke & Calcined Petroleum Coke<\/h2>\n

    Using high quality low sulfur petroleum coke as raw material, produced by graphitization process, it is used for carburization of various electric furnace melting cast steel and cast iron. It has high purity, excellent particle morphology and graphitized hexagonal crystal structure. It not only plays the role of carburization, but also promotes the inoculation and nucleation of cast iron, improves graphite morphology, increases the number of graphite balls, and improves the mechanical properties and processing properties of materials. According to the sulfur content, it can be divided into three levels: low sulfur, medium sulfur and high sulfur.<\/p>\n

    Chemical specification: fixed carbon: 98-99%, sulfur content: 0.05-0.2%;<\/p>\n

    Particle size : 1-5mm\/1-3mm\/0-3mm<\/p>\n

    \"GPC
    GPC 1-5MM C 98.5% min,S 0.05%max<\/figcaption><\/figure>\n

    HOW TO USE of Graphite Petroleum Coke\/Calcined Petroleum Coke:<\/h3>\n

    1. Place the carburizer in the middle and lower part of the electric furnace. That is to say, after a small part of iron charge is placed in the furnace to melt it (or a small amount of hot metal is left on the furnace), the required metal charge is added, and the carburizing agent is fully pressed into the hot metal to make the carburizing agent fully contact with the hot metal.<\/p>\n

    2. During the absorption period of carburizer, slag removal operation of hot metal should be avoided to prevent carburizer from being taken out of the furnace with slag.<\/p>\n

    3. It is suggested that the recycled material or pig iron should be added after the carburizing agent is removed.<\/p>\n

    4. Before the hot metal is discharged from the furnace, a small amount of carburizing agent can be added to the surface of the hot metal for micro carbon transfer, and the carburizing agent can be dissolved and absorbed by eddy current stirring or manual stirring.<\/p>\n

    5. Increasing silicon and sulfur should be carried out after the absorption of carburizer.<\/p>\n

    \n

    Calcined coal carburizing agent\/Calcined anthracite<\/h2>\n

    With high quality anthracite as raw material, the direct current calciner is used to calcine at high temperature above 2000 \u2103<\/p>\n

    In addition to the moisture and volatile matter in coal, it improves the density and conductivity of anthracite, enhances the mechanical strength and oxidation resistance, and has good characteristics of low ash content and high density. Anthracite carburizer is the raw material for manufacturing high quality carbon products, which is used as carbon additive or fuel in iron and steel industry. Main raw materials of anthracite carburizer<\/p>\n

    High quality anthracite has the characteristics of low ash and low sulfur. Carbon additive has two main uses, namely as fuel and carbon additive.<\/p>\n

    \"Calcined
    Calcined anthracite carburizer 1-5mm<\/figcaption><\/figure>\n

    Chemical specification: fixed carbon: 90-95%, sulfur content: 0.3-0.5%;<\/p>\n

    Particle size : 1-5mm\/1-3mm\/0-3mm<\/p>\n

    Each batch of goods need to be strictly tested. In terms of quality control system, we have achieved the best system in the same industry. We provide our own test results while supporting any third-party testing requirements, enable helping our partners to ensure the quality of supply in multual ways.<\/h5>\n
    \n

    <\/h3>\n

    Size:<\/h3>\n

    0-3mm,1-5mm or other size accoriding to customer’s request.<\/h2>\n
    \"graphite
    graphite petroleum coke<\/figcaption><\/figure>\n

    Packing:<\/h3>\n

    25kg\/50kg\/1mt\/1.25mt PP bag<\/h2>\n
    \"carbon
    carbon riser(GPC) loading in 20ft container<\/figcaption><\/figure>\n

    Welcome customer to discuss cooperation with us.Mutual benefit and win-win, long-term stable supply of high-quality low-cost carburizer.<\/h4>\n

    www.brightferroalloy.com<\/a><\/p>\n